Showing all 6 results
-
TAURUS ALUMINIUM TIG ROD 4043-1.6MM
Description TAURUS TIG 4043 is a 95% aluminium, 5% silicon rod suitable for welding heat treatable base alloys. It has a lower melting point and more fluidity and is preferred by welders because of its favourable operating characteristics. The ER4043 rod is also less sensitive to weld cracking. TAURUS TIG 4043 should be used with…
-
TAURUS ALUMINIUM TIG ROD 4043-2.4MM
Description TAURUS TIG 4043 is a 95% aluminium, 5% silicon rod suitable for welding heat treatable base alloys. It has a lower melting point and more fluidity and is preferred by welders because of its favourable operating characteristics. The ER4043 rod is also less sensitive to weld cracking. TAURUS TIG 4043 should be used with…
-
TAURUS ALUMINIUM TIG ROD 4043-3.2MM
Description TAURUS TIG 4043 is a 95% aluminium, 5% silicon rod suitable for welding heat treatable base alloys. It has a lower melting point and more fluidity and is preferred by welders because of its favourable operating characteristics. The ER4043 rod is also less sensitive to weld cracking. TAURUS TIG 4043 should be used with…
-
TAURUS ALUMINIUM TIG ROD 5356-1.6MM
Description TAURUS TIG 5356 is a 95% aluminium, 5% magnesium rod for general purpose welding when 40 000 psi tensile strength is not required. TAURUS TIG 5356 should be used with a zirconated tungsten electrode with pure argon or an argon-helium mixture for thick sections, at a flow rates of 10 – 15 l/min. For…
-
TAURUS ALUMINIUM TIG ROD 5356-2.4MM
Description TAURUS TIG 5356 is a 95% aluminium, 5% magnesium rod for general purpose welding when 40 000 psi tensile strength is not required. TAURUS TIG 5356 should be used with a zirconated tungsten electrode with pure argon or an argon-helium mixture for thick sections, at a flow rates of 10 – 15 l/min. For…
-
TAURUS ALUMINIUM TIG ROD 5356-3.2MM
Description TAURUS TIG 5356 is a 95% aluminium, 5% magnesium rod for general purpose welding when 40 000 psi tensile strength is not required. TAURUS TIG 5356 should be used with a zirconated tungsten electrode with pure argon or an argon-helium mixture for thick sections, at a flow rates of 10 – 15 l/min. For…